- 4 -

Adhesive*

6mm Nozzle

gms/minute

10mm Nozzle

gms/minute

Scotch-Weld epoxy adhesive DP110 Gray

Scotch-Weld epoxy adhesive DP110 Gray 100°F (38°C)

8.3

14.0

31.5

50.3

Epoxy Adhesives

DP110 Translucent and Gray

Environmental

Resistance

Note: The following technical information and data should be considered representative

or typical only and should not be used for specification purposes.

Overlap shear specimens were prepared on aluminum as above and exposed to the

environment conditions described below.

Environment

Overlap Shear (psi) @ 75°F (24°C)

3M™ Scotch-Weld™

Epoxy Adhesive

DP110 Translucent

3

M™ Scotch-Weld™

Epoxy Adhesive

DP110 Gray

Etched

Abraded

Etched

Abraded

Initial

2500

1000

2500

2300

30 days tap water @ 75°F (24°C)

2300

1250

2300

1250

3 days, 160°F (71°C), 100% rel. humidity

1200

700

1200

700

14 days in 5% salt spray @ 95°F (35°C)

500

150

500

150

Note: Avoid using either Scotch-Weld epoxy adhesive DP110 Translucent or Gray on metals

where the bonded parts will experience high humidity/hot water conditions. User must test

thoroughly adhesive performance for any environments which will be encountered.

3M™ EPX™

Pneumatic Applicator

Delivery Rates

400 ml Applicator – Maximum Pressure 73 psi

200 ml Applicator – Maximum Pressure 58 psi

Scotch-Weld epoxy adhesive DP110 Gray

6.6

25.6

Scotch-Weld epoxy adhesive DP110 Gray 100°F (38°C)

35.1

115.9

Scotch-Weld epoxy adhesive DP110 Gray 125°F (49°C)

53.8

129.6

Scotch-Weld epoxy adhesive DP110 Gray 150°F (66°C)

332.0

687.0**

48.5/50 ml Applicator – Maximum Pressure 50 psi

Adhesive*

1/4 in. Nozzle

gms/minute

Scotch-Weld epoxy adhesive DP110 Translucent

Scotch-Weld epoxy adhesive DP110 Gray

6.3

6.2 (nozzle cut back 2 divisions)

12.3

12.1 (nozzle cut back 2 divisions)

*Tests were run at a temperature of 70°F ± 2°F (21°C ± 1°C) and at maximum applicator pressure.

**Did not mix adequately.