- 4 -

Typical Performance

Characteristics

Note: The following technical information and data should be considered representative

or typical only and should not be used for specification purposes.

3M™ VHB™ Tapes

Family

Product

Number

Colour

Thickness

Inches

4919F

Black

0.025

17 (30)

90 (620)

80 (550)

4926

Grey

0.015

14 (25)

95 (660)

90 (620)

4936(F)

Grey

0.025

17 (30)

90 (620)

80 (550)

4941(F)

Grey

0.045

22 (39)

85 (590)

70 (480)

4947F

Black

0.045

22 (39)

85 (590)

70 (480)

4956(F)

Grey

0.062

22 (39)

80 (550)

70 (480)

4979F

Black

0.062

22 (39)

80 (550)

70 (480)

4991

Grey

0.090

22 (39)

70 (480)

65 (450)

4991B

Black

0.090

22 (39)

70 (480)

65 (450)

RP16(F)

Grey

0.016

12 (21)

95 (660)

90 (620)

RP25F)

Grey

0.025

17 (30)

90 (620)

80 (550)

RP32F)

Grey

0.032

18 (32)

85 (590)

75 (520)

RP45(F)

Grey

0.045

20 (35)

85 (590)

70 (480)

RP62(F)

Grey

0.062

20 (35)

80 (550)

70 (480)

5906

Black

0.006

9 (16)

100 (690)

100 (690)

5907

Black

0.008

10 (18)

100 (690)

100 (690)

5908

Black

0.010

12 (21)

100 (690)

100 (690)

5909

Black

0.012

12 (21)

100 (690)

100 (690)

5915(P)

Black

0.016

14 (25)

90 (620)

90 (620)

5915WF

White

0.016

14 (25)

90 (620)

90 (620)

5925(P)

Black

0.025

17 (30)

90 (620)

90 (620)

5925WF

White

0.025

17 (30)

90 (620)

90 (620)

5930(P)

White

0.032

19 (33)

90 (620)

85 (590)

5930WF

Black

0.032

19 (33)

90 (620)

85 (590)

5952(P)

Black

0.045

22 (39)

90 (620)

80 (550)

5952WF

White

0.045

22 (39)

90 (620)

80 (550)

5958FR

Black

0.040

20 (35)

100 (690)

100 (690)

5962(P)

Black

0.062

22 (39)

90 (620)

80 (550)

5962WF

White

0.062

22 (39)

90 (620)

80 (550)

Dynamic Adhesion Performance

90° Peel Adhesion

lb/in N/cm

Normal Tensile

Dynamic Overlap Shear

90° Peel Adhesion - Based on ASTM D3330 -To stainless steel, room temperature, jaw speed 12 in/min (304.8 mm/min). Average force to

remove is measured. 72 hour dwell.

force to separate is measured. 72 hour dwell.

force to separate is measured. 72 hour dwell.

XXXXX